Reflow Recycled PLA - Monochrome Collection 2.85mm
Flexural strain at break % 3.6 ISO 178
SAMPLE PREPARATION AND TESTING CONDITIONS
Sample preparation conditions:
Ultermaker 2 with 0.4 mm nozzle was applied for preparing both tensile and flexural
specimens. Line width: 0.35 mm - layer height: 0.2 mm - Printing speed: 15 mm/s -
retraction distance and speed: 4 mm and 40 mm/s - printing temperature : 220 ºC
Testing conditions:
Five samples were tested and the value shared was the average value.
For tensile specimens, they were printed flatly (x-y direction ) and the printing direction
was in line with the tensile stretching direction. As for the flexural specimens, the printing direction was perpendicularly to the test direction.
DISCLAIMER
The values and recommendations provided herein are given or accepted at your own risk. In view of variations in maintenance, processing, and neither Reflow nor its a"liates make any warranty relating to it or because of it. Neither Reflow nor its a"liates shall be responsible for the use of this information, or of any product, method or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability or fitness of any product; and nothing herein waives any of
Reflow’s conditions of sale. Specifications are subject to adaptation without prior notice.
0
0
SAMPLE PREPARATION AND TESTING CONDITIONS
Sample preparation conditions:
Ultermaker 2 with 0.4 mm nozzle was applied for preparing both tensile and flexural
specimens. Line width: 0.35 mm - layer height: 0.2 mm - Printing speed: 15 mm/s -
retraction distance and speed: 4 mm and 40 mm/s - printing temperature : 220 ºC
Testing conditions:
Five samples were tested and the value shared was the average value.
For tensile specimens, they were printed flatly (x-y direction ) and the printing direction
was in line with the tensile stretching direction. As for the flexural specimens, the printing direction was perpendicularly to the test direction.
DISCLAIMER
The values and recommendations provided herein are given or accepted at your own risk. In view of variations in maintenance, processing, and neither Reflow nor its a"liates make any warranty relating to it or because of it. Neither Reflow nor its a"liates shall be responsible for the use of this information, or of any product, method or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability or fitness of any product; and nothing herein waives any of